Technical Data Sheet 技术数据表
KYC-DA10
Chemical composition 化学成分
Adipate plasticizer
己二酸增塑剂
Specifications 规格说明
Characteristics 特性 | Unit 单位 | Specification 规格 | Test Method 测试方法 |
Appearance 外观 | - | Limpid liquid 透明液体 | Visual 目测 |
Colour 色度 | Pt-Co | 30 max | ASTM D 1045 |
Acid Value 酸值 | mgKOH/g | 0.07 max | GB/T 1668 |
Water Content 水分含量 | wt.% | 0.10 max | ASTM E 1064 |
Density 密度（20°C） | g/ml | 0.905-0.908 | ASTM D 4052 |
Flash Point(Open) 闪点（开口杯法） | °C | 200 min | GB/T 1671 |
Ester Content 酯含量 | wt.% | 99.5 min | G.C |
Alcohol Content 醇含量 | ppm | 1000 max | G.C |
Total Contents of Phthalates 邻苯类总含量 | ppm | 1000 max | G.C |
Liquid Properties液体性能
Temperature温度 (°C) | Brookfield Viscosity博勒飞粘度 (mPa·s) |
5 | 110 |
15 | 55 |
25 | 25 |
35 | 9 |
45 | 5 |
55 | 4 |
65 | 3 |
75 | 2 |
The figures above are typical values and are not intended as specification limits.
以上数据是典型数值只供参考，而不是技术指标规范。
Brief Descriptions 产品简介
KYC-DA10 is a colorless oily limpid liquid with a characteristic odour. It is miscible with common organic solvents, immiscible with water and miscible with most of the plasticizers used in the processing of PVC.
KYC-DA10一种无色油状透明液体，具有独特的气味。能溶于大部分有机溶剂，但不溶于水，与大部分增塑剂混溶用于PVC工艺的加工。
The product KYC-DA10 due to its nature does not have a shelf life. However, it can be stored in appropriate containers at a temperature of approximately 25°C and the exclusion of humidity for at least 1 year, without losing its chemical properties. Nevertheless, re-testing of properties is recommended every 6 month from the production date.
KYC-DA10由于其特性没有设定储存期。但是在温度大约为25℃且有效除湿的条件下，将其储存于适当的容器内至少一年不会失去其化学特性。不过我们仍建议在未使用的每六个月应重新检验，以获得最佳的使用效果。
For further information on the characteristics and properties of KYC-DA10 in the liquid state, see the relevant
standard Materials Safety Data Sheet.
如需有关KYC-DA10的液态特性和性能的更多信息，请参阅相关标准「物质安全数据表」(MSDS)。
Characteristics and Applications of KYC-DA10
KYC-DA10 的特性及应用
KYC-DA10 can be used in a wide range of applications for such as:
KYC-DA10的应用范畴广阔，其中包括：
KYC-DA10 is a plasticizer for PVC, its co-polymers and synthetic rubber, the main characteristic of which is to
confer excellent performance at low temperatures.
When used for the preparation of plastisol it confers initial low viscosity and good stability of the latter over time.
It is most commonly used in combination with high-molecular-weight phthalic esters.
KYC-DA10是PVC及其共聚物和合成橡胶的增塑剂，其主要特点为其优异的耐低温性能。
当用于制备塑性溶胶时，它具有初始低粘度和较好的塑性溶胶稳定性。
它最常与高分子量的邻苯二甲酸酯结合使用。
KYC-DA10 is typically used in典型用途为:
Gaskets垫圈;
Electrical cables for low temperatures低温电缆；
Cold resistant agricultural film耐寒农用薄膜；
Artificial leather人造革；
Outdoor water pipe户外用水管；
Frozen food packaging film冷冻食品包装膜；
Compounds for footwear鞋类复合材料。
KYC-DA10 is a technical grade product. Should you have more specific needs, you are invited to contact our sales offices or representative agencies.
KYC-DA10是一款技术级产品。如果您有更具体的需求，请与我们的销售办事处或代理机构联系。
General properties in PVC compounds 在PVC化合物中的一般特性
The properties of KYC-DA10 were evaluated in comparison with DOS by the following formulation:
用如下配方，将KYC-DA10与DOS的性能进行比较如下：
Formulation 配方 | (parts by weight 按重量分配) |
PVC S-70聚氯乙烯 | 100 |
Main Plasticizer主增塑剂DOTP | 47 |
Auxiliary Plasticizer辅增塑剂 | 18 |
Calcium carbonate碳酸钙 | 40 |
Ca/ Zn stabilizer钙/锌稳定剂 | 4 |
PE-WAX聚乙烯蜡 | 0.6 |
The specimens were prepared by calendering and moulding to obtain the thickness required for the different test methods.
采用密炼、压制和制模工艺以取得不同测试方法所需厚度的试片。
Results 结果
Test Items 测试项目 | Unit 单位 | Test Method 测试方法 | KYC-DA10 | DOS |
SHORE A 邵氏硬度A | A | GB 2411 | 79 | 79 |
Specific gravity 比重 | g/cm3 | GB/T 1033 | 1.343 | 1.345 |
Tensile Strength 抗张强度 | MPa | GB/T 1040 | 16.8 | 16.3 |
Elongation at break 断裂伸长率 | % | GB/T 1040 | 323 | 299 |
Air ageing Condition 空气老化条件 | 100℃×168h | |||
Change of Tensile Strength 拉伸强度变化率 | % | GB/T 8815 | 2.7 | 3.7 |
Change of Elongation at break 断裂伸长率变化率 | % | GB/T 8815 | 3.0 | 6.8 |
Low-temperature impact embrittlement 低温冲击脆化 | -40℃ | GB/T 5470 | Pass 通过 | Pass 通过 |
Volume Resistivity at 20℃ 体积电阻率20℃ | Ω·m | GB/T 1410 | 3.9×108 | 3.6×108 |
Thermal stability time at 200℃ 200℃热稳定时间 | min 分钟 | GB/T 2951 | 107 | 112 |
Heat aging mass loss 热老化质量损失 100℃×168H | g/m2 | GB/T 2951 | 3.0 | 3.0 |
In the tests according to the standard GB/T 8815, compounds were aged in an Natural ventilation oven.
此测试按照国家标准GB/T 8815，复合物在自然换气老化箱内进行老化处理。
The information contained here is correct and accurate and is based on our technical and scientific knowledge at the date of going to press.
本数据所含信息是正确和准确的，是基于我们在出版前对技术和科学知识的总结。
Such information is, in all cases, relevant only with respect to the product as used in its pure state and only for the uses referred to in this publication.
所含信息仅限于所用产品为纯物质的情况下，此刊物仅供用户参考。
Nothing stated here may be taken or construed as implying a breach of existing patents.
任何陈述都不应被视为或理解为侵犯已有的专利。
No warranty, either expressed or implicit, is given with regard to the results to be obtained from using this information.
任何所述或所喻，本公司不对使用此信息造成的后果承担责任。